Graphite
Packing 
Graphite
Category: Spare Part
Product Style Number & Name:
SP3010 Hot-pressed graphite
SP3020 Carbon-graphite
SP3010 Hot-pressed graphite
Hot-pressed graphite is made from the mixture of high-purity graphite powder, resin and other additives, which are hot pressed and solidified in mould. It is widely applied in clear water medium, in water seal devices of automobiles, small pumps, household electrical equipments, etc.
SP3020 Carbon-graphite
Carbon-graphite has the advantages of good resistance to corrosion, wear and high temperature, good self-lubricity and heat conductivity, low friction factor and expansion coefficient. It is the ideal friction material used in various mechanical seals.
SP3010 Hot-pressed graphite
|
Density |
1.65g/cm3 |
|
Hardness |
≥55 (HS) |
|
Compression strength |
≥135Mpa |
|
Bend strength |
50Mpa |
SP3020 Carbon-graphite
|
Material |
Density |
Bending strength |
Compression strength |
Hardness |
Porosity |
|
|
Epoxy resin impregnated (H) |
M106H |
1.75g/cm3 |
65Mpa |
200Mpa |
85 (HS) |
2.5% |
|
M120H |
1.70g/cm3 |
60Mpa |
180Mpa |
80 (HS) |
2.5% |
|
|
M205H |
1.70g/cm3 |
60Mpa |
200Mpa |
70 (HS) |
2.5% |
|
|
M252H |
1.72g/cm3 |
45Mpa |
120Mpa |
45 (HS) |
2.5% |
|
|
Furan resin impregnated (K) |
M106K |
1.75g/cm3 |
67Mpa |
200Mpa |
90 (HS) |
2.0% |
|
M120K |
1.70g/cm3 |
62Mpa |
180Mpa |
85 (HS) |
2.0% |
|
|
M205K |
1.70g/cm3 |
62Mpa |
180Mpa |
75 (HS) |
2.0% |
|
|
M252K |
1.72g/cm3 |
47Mpa |
120Mpa |
48 (HS) |
2.0% |
|
|
KC170 |
1.82g/cm3 |
68Mpa |
200Mpa |
80 (HS) |
2.0% |
|
|
Phenol aldehyde resin impregnated (F) |
M106F |
1.75g/cm3 |
60Mpa |
200Mpa |
85 (HS) |
2.0% |
|
M120F |
1.70g/cm3 |
55Mpa |
180Mpa |
80 (HS) |
2.0% |
|
|
M205F |
1.70g/cm3 |
55Mpa |
200Mpa |
70 (HS) |
2.0% |
|
|
M252F |
1.72g/cm3 |
40Mpa |
120Mpa |
45 (HS) |
2.0% |
|
|
KC573 |
1.85g/cm3 |
85Mpa |
370Mpa |
110 (HS) |
2.0% |
|
|
KC673 |
1.87g/cm3 |
78Mpa |
245Mpa |
87 (HS) |
2.0% |
|
|
Antimony |
M104D |
2.25g/cm3 |
99Mpa |
340Mpa |
90 (HS) |
0.57% |
Customized sizes.